[1]白强,霍富永,孙彦虎,等.聚乙烯内衬复合油管失效分析[J].石油管材与仪器,2020,6(03):47-50.[doi:10.19459/j.cnki.61-1500/te.2020.03.012]
 BAI Qiang,HUO Fuyong,SUN Yanhu,et al.Failure Analysis of Polyethylene Lined Tubing[J].Petroleum Tubular Goods & Instruments,2020,6(03):47-50.[doi:10.19459/j.cnki.61-1500/te.2020.03.012]
点击复制

聚乙烯内衬复合油管失效分析
分享到:

《石油管材与仪器》[ISSN:2096-0077/CN:61-1500/TE]

卷:
6
期数:
2020年03期
页码:
47-50
栏目:
失效分析与预防
出版日期:
2020-06-20

文章信息/Info

Title:
Failure Analysis of Polyethylene Lined Tubing
文章编号:
2096-0077(2020)03--0047-04
作者:
白强1 霍富永2孙彦虎3魏斌1
1.中国石油集团石油管工程技术研究院,石油管材及装备材料服役行为与结构安全国家重点实验室 陕西 西安 710077;2.西安长庆科技工程有限责任公司 陕西 西安 710021; 3.长庆油田分公司第四采油厂 陕西 榆林 718500
Author(s):
BAI Qiang1 HUO Fuyong2 SUN Yanhu3 WEI Bin1
1. State Key Laboratory for Performance and Structure Safety of Petroleum Tubular Goods and Equipment Materials, CNPC Tubular Goods Research Institute,Xi′an,Shaanxi 710077,China;2. Xi′an Changqing Technology & Engineering Co.Ltd., Xi′an,Shaanxi 710021, China;3.No.4 Oil Production Plant,PetroChina Changqing Oilfield Company,Yulin,Shaanxi 718500,China
关键词:
聚乙烯内衬复合油管塌陷失效分析
Keywords:
polyethylene liner composite tubing collapse failure analysis
分类号:
TE358
DOI:
10.19459/j.cnki.61-1500/te.2020.03.012
文献标志码:
A
摘要:
由于聚乙烯内衬油管内衬塌陷,导致抽油杆接箍对油管塌陷处产生切削作用,丝条状的切削物缠绕在泵体上导致卡泵事故发生。为了查明内衬塌陷原因,对现场服役的聚乙烯内衬复合油管进行检测评价。通过现场调研、理化性能检测、并结合油管制造和使用情况,明确了油管塌陷失效事故原因。结果表明:由于内衬复合油管管端位置处的内衬翻边工艺控制不当,在复合油管运行过程中,内衬管随着所处环境温度波动而发生热胀冷缩,但其行为与油管基体热胀冷缩并不协调,导致端部翻边处的密封失效。随着运行时间的增加,更多介质从内衬复合油管管端翻边处渗漏到夹层间,最终导致其间压力大于复合管内部压力而发生内衬坍塌。基于失效原因分析,提出了相应的质量控制建议。通过本次失效分析,为今后内衬复合油管生产和应用提供借鉴。
Abstract:
Due to the collapse of the liner of the polyethylene lined tubing, the rod collar has a cutting effect on the collapse of the tubing, and the slip-like cutting winds on the pump body, which leads to the accident of stuck pump. In order to find out the cause of inner liner collapse, the polyethylene lined tubing in service was tested and evaluated. Failure causes were investigated through field investigation, physical and chemical properties testing combined with analysis of the service conditions. Results show that the failure of sealing at flanged end of liner composite tubing due to improper process control is the direct cause of lining tubing collapse. The lining tubing expands and contracts with the fluctuation of the ambient temperature during operation. However, its behavior is not consistent with the thermal expansion and cold contraction of the tubing. With the increase of running time, more media leaks from the flanging of the end of the liner composite tubing to the interlayer. Finally, the inner lining collapse because the pressure is greater than the inner pressure of the composite tubing. Based on the analysis of failure reasons, the corresponding quality control suggestions were put forward. The failure analysis results can also provide reference for the production and application of this kind of tubing in the future.

参考文献/References:

[1] 高玉森,张爱华,常大胜,等.超高分子量聚乙烯内衬复合油管制备工艺技术[J]. 石油矿场机械,2015,44(7):98-101.
[2] 李郁蕊.萨北油田超高分子量聚乙烯内衬油管应用与效果评价[J]. 化学工程与装备,2019,48(6):132-135.
[3] 尹瑞新,李彬.PE100内衬油管在大港南部油田偏磨腐蚀抽油机井的应用[J]. 中国石油和化工标准与质量,2017,37(21):152-155.
[4] 蔡雪华,李厚补,戚东涛,等.油气田用复合管非金属内衬材料性能分析[J]. 石油管材与仪器,2017,3(2):28-31.
[5] 韩方勇,丁建宇,孙铁民,等.油气田应用非金属管道技术研究[J]. 石油规划设计,2012,23(6): 5-9.
[6] 刘伟,孙自成,程占全,等.复杂井筒内衬油管防磨技术应用研究[J]. 石化技术,2016,23(6):161-162.
[7] 齐国权,刘正东,戚东涛,等.气体在增强热塑性塑料管道中渗透行为控制研究[J]. 石油管材与仪器,2017,3(2):58-61.
[8] 李波.超高摩尔质量聚乙烯内衬复合管应用前景展望[J]. 塑料工业,2006,34(12):1-3.

备注/Memo

备注/Memo:
第一作者简介:白强,男,1984年生,高级工程师,2010年毕业于西安交通大学机械工程专业,目前主要从事油井管新产品开发与转化工作。E-mail:baiqiang@cnpc.com.cn
更新日期/Last Update: 2020-06-25