[1]丛深,王志东,蔡克,等.某油田ERW钢管管体泄漏失效分析[J].石油管材与仪器,2020,6(01):60-64.[doi:10.19459/j.cnki.61-1500/te.2020.01.015]
 CONG Shen,WANG Zhidong,CAI Ke,et al.Leakage Failure Analysis of the ERW Steel Pipeline in an Oilfield[J].Petroleum Tubular Goods & Instruments,2020,6(01):60-64.[doi:10.19459/j.cnki.61-1500/te.2020.01.015]
点击复制

某油田ERW钢管管体泄漏失效分析
分享到:

《石油管材与仪器》[ISSN:2096-0077/CN:61-1500/TE]

卷:
6
期数:
2020年01期
页码:
60-64
栏目:
失效分析与预防
出版日期:
2020-02-25

文章信息/Info

Title:
Leakage Failure Analysis of the ERW Steel Pipeline in an Oilfield
文章编号:
2096-0077(2020)01--0060-05
作者:
丛深1王志东2蔡克1瞿婷婷1仝珂1陈志昕1
1.中国石油集团石油管工程技术研究院 陕西 西安 710077;2.中国石油长庆油田分公司物资供应处(物资管理部) 陕西 西安 710016
Author(s):
CONG Shen1 WANG Zhidong2 CAI Ke1 QU Tingting1 TONG Ke1 CHEN Zhixin1
1.CNPC Tubular Goods Research Institute, Xi′an, Shaanxi 710077, China;2.Material Supplying Department, Changqing Oilfield Company, PetroChina, Xi′an, Shaanxi 710016, China
关键词:
ERW钢管膜下腐蚀穿孔刺漏失效分析
Keywords:
ERW steel pipeline underdeposit corrosion leakage failure analysis
分类号:
TE988
DOI:
10.19459/j.cnki.61-1500/te.2020.01.015
文献标志码:
A
摘要:
为分析东北某油田ERW钢管在输送油气过程中管体泄漏失效原因,对ERW钢管失效样品进行宏观形貌检验、理化检验、金相组织及扫描电镜分析等试验。结果表明,该ERW钢管管体泄漏失效的主要原因是管道底部残留积液和空气试压中的O2和CO2导致的腐蚀,腐蚀介质为大体积的O2和CO2在小体积的残留积液中形成持续饱和的腐蚀性水溶液,腐蚀类型为腐蚀产物膜的膜下腐蚀。建议对后续再建管线,试压前对管线进行热风吹扫;如果管线不及时投用,建议采用氮气保压。
Abstract:
This paper gives a thorough investigation on the leakage reason of the ERW steel pipeline in an oil field. Through appearance inspection, physical and chemical inspection, metallographic inspection and scanning electron microscope (SEM), it is shown that the main reason is corrosion caused by residual liquid at the bottom of the pipeline and O2 and CO2 during air pressure test. The corrosion medium is large volume of O2 and CO2 forming continuously saturated corrosive aqueous solution in small volume of residual liquid, and the corrosion type is underdeposit corrosion. It is recommended to conduct hot air purging before pressure test for future pipelines. If the pipeline is not put into use in time, it is recommended to use nitrogen to maintain pressure.

参考文献/References:

[1] 郭益,张璐,张维臣,等.ERW钢管在气田集输干线中的应用[J].油气储运,2011,29(5):21-23.
[2] 李记科,严实春,徐爱军,等.高质量ERW钢管可用作天然气输送管[J].焊管,2007,30(2):72-75.
[3] 孙永喜.ERW钢管在长输管道建设中的应用[J].油气储运,2001,20(4):47-49.
[4] 李记科,齐宝钗,高建忠.国内ERW钢管生产情况[J].焊管,2006,29(6):63-67.
[5] 潘家华.ERW钢管的发展前景和面临的课题[J].焊管,1989,12(3):1-3.
[6] 李磊,林凯,李孝军,等.西部某油田S135钻杆管体断裂失效分析[J].金属热处理,2015,40(S):247-249.
[7] 彭在美,窦树柏.试论我国高品质ERW焊管发展的技术路线[J].钢管,2008,37(3):9-12.
[8] 史福忠,马建国,陈燕军.ERW焊管焊缝热影响区性状与焊管质量的相关性初探[J].焊管,2007,30(3):60-62.
[9] 毕洪运,陆明和.ERW直缝焊管焊缝形态与金相检验评价[J].宝钢技术,2006(3):23-26.
[10] 介升旗.高频焊管常见焊接缺陷分析[J].焊管,2003(4):47-51,62.

备注/Memo

备注/Memo:
第一作者简介:丛深,男,1991年生,工程师,2015年毕业于英国曼彻斯特大学材料工程学专业,获硕士学位,现主要从事石油管失效分析工作。E-mail:congshen@cnpc.com.cn
更新日期/Last Update: 2020-02-25