某热煨弯管开裂原因分析
分享到:

《石油管材与仪器》[ISSN:2096-0077/CN:61-1500/TE]

卷:
5
期数:
2019年03期
页码:
38-41
栏目:
失效分析与预防
出版日期:
2019-06-20

文章信息/Info

Title:
Cracking Analysis of Induction Heat Bend Pipe
文章编号:
2096-0077(2019)03--0038-04
作者:
李丽锋12张哲3常大伟4朱丽霞1武刚1张庶鑫1
1.中国石油集团石油管工程技术研究院 陕西 西安 710077;2.中国石油大学(华东) 山东 青岛 257061; 3.中国石油新疆油田公司 新疆 克拉玛依 834000;4.中国石油西气东输管道公司 上海 200000
Author(s):
LI Lifeng12 ZHANG Zhe3CHANG Dawei4ZHU Lixia1WU Gang1 ZHANG Shuxin1
1.CNPC Tubular Goods Research Institute,Xi′an,Shaanxi 710077,China;2.China University of Petroleum,Qindao,Shandong 257061,China;3.PetroChina Xinjiang Oilfield Company,Karamay,Xinjiang 834000,China;4.PetroChina West East Gas Pipeline Company, Shanghai 200000, China
关键词:
热煨弯管马氏体脆性回火正火
Keywords:
induction heat bend pipemartensitebrittlenesstempernormalize
分类号:
TE832;TG115
DOI:
10.19459/j.cnki.61-1500/te.2019.03.009
文献标志码:
A
摘要:
采用宏观分析、无损检测、化学成分分析、力学性能检测、金相分析和扫描电镜等试验,分析了弯管开裂原因,并对弯管开裂处材料分别进行了550 ℃、650 ℃的回火和900 ℃的正火热处理。结果表明:失效弯管起裂于外表面,并向内表面脆性扩展,开裂主要是由于弯管热煨工艺不当,产生硬而脆的马氏体组织,弯管抗脆性断裂能力严重不足所致;回火或正火热处理工艺后,弯管开裂处材料硬度明显下降,冲击韧性显著提高,性能得到改善,建议选用正火钢材用水冷却煨制的感应加热弯管,应在水冷后进行正火或回火热处理。
Abstract:
The cracking reason on induction heat bend pipe was analyzed through macroscopic analysis,nondestructive testing,chemical composition analysis, mechanical properties testing,metallographic analysis, scanning electron microscopy and other means,and the heat treatment on tempering at 550 ℃ or 650 ℃ and normalizing at 900 ℃ were carried out for the bend materials. The results show that the crack initiates from the outer surface and propagates brittlely to the inner surface, and the main reason for cracking is that the induction heat process of bend pipe is improper, which can result in the production of brittle martensite structure, and the brittle fracture resistance of bend pipe is seriously inadequate. After tempering or normalizing, the hardness obviously decreases, the impact toughness increases and the properties are improved. It is suggested that the induction heat bend pipe made of normalizing steel by water cooling should be retempered or renormalized after watercooling.

参考文献/References:

[1] 刘迎来,许彦,王高峰,等.小口径感应加热弯管低应力脆断原因分析及控制措施研究[J]. 金属热处理,2015(9),40:223-227.
[2] 路彩红,李金凤,仝珂,等.X65弯管渗漏失效分析[J]. 金属热处理,2015(10),40:274-280.
[3] 仝珂,谢学东,李亮,等.油气输送用弯管失效原因及典型案例分析[J]. 石油管材与仪器,2016,2(01):46-49.
[4] 马宗耀,田伟.16Mn钢油气集输管线弯管失效分析[J]. 金属热处理,2009(3),34(3):89-92.
[5] 潘鸿,吕文涛,钱英豪,等.L360钢级弯管开裂失效分析[J]. 热加工工艺,2016(4),45(8):253-255.
[6] 石油管材专业标准化技术委员会.油气输送用钢制感应加热弯管:SY/T 5257—2012[S]. 北京 :石油工业出版社,2013.
[7] 全国钢标准化技术委员会.高压化肥设备用无缝钢管:GB 6479—2000[S]. 北京 :中国标准出版社,2000.

相似文献/References:

[1]郭嗣杰,林坤.石油测井仪器外壳焊接工艺探究[J].石油管材与仪器,2016,(06):90.
 GUO Sijie,LIN Kun.Welding Procedure Exploration of Well Logging Tool Shell[J].Petroleum Tubular Goods & Instruments,2016,(03):90.

备注/Memo

备注/Memo:
第一作者简介:李丽锋,男,1983年生,高级工程师,2008年毕业于 北京 航空航天大学材料学专业,获硕士学位,主要从事油气管道及储运设施风险评估、检测评价及失效分析方面的研究。E-mail:lilifeng004@cnpc.com.cn
更新日期/Last Update: 2019-06-25